Pajonk G (1989) Drying methods preserving the textural properties of gels. Ochoa M, Lamy-Mendes A, Maia A, Portugal A, Durães L (2019) Influence of structure-directing additives on the properties of poly (methylsilsesquioxane) aerogel-like materials. Mathieu B, Blacher S, Pirard R, Pirard J, Sahouli B, Brouers F (1997) Freeze-dried resorcinol-formaldehyde gels. Martin J, Hosticka B, Lattimer C, Norris P (2001) Mechanical and acoustical properties as a function of PEG concentration in macroporous silica gels. Ma H, Zheng X, Luo X, Yi Y, Yang F (2018) Simulation and analysis of mechanical properties of silica aerogels: from rationalization to prediction. Ma X, Sun H, Yu P (2008) A novel way for preparing high surface area silica monolith with bimodal pore structure. Liu M-L, Yang D-A, Qu Y-F (2010) Effect of different chemical additives and heat-treatment on ambient pressure dried silica aerogels. Klvana D, Chaouki J, Repellin-Lacroix M, Pajonk G (1989) A new method of preparation of aerogel-like materials using a freeze-drying process. Kim CE, Yoon JS, Hwang HJ (2009) Synthesis of nanoporous silica aerogel by ambient pressure drying. Katti A, Shimpi N, Roy S, Lu H, Fabrizio EF, Dass A, Capadona LA, Leventis N (2006) Chemical, physical, and mechanical characterization of isocyanate cross-linked amine-modified silica aerogels. Johnson LM, Gao L, Shields Iv CW, Smith M, Efimenko K, Cushing K, Genzer J, López GP (2013) Elastomeric microparticles for acoustic mediated bioseparations. Huang Y, He S, Feng M, Dai H, Pan Y, Cheng X (2019) Organic solvent-saving preparation of water glass based aerogel granules under ambient pressure drying. Hegde ND, Rao AV (2007) Physical properties of methyltrimethoxysilane based elastic silica aerogels prepared by the two-stage sol–gel process. He S, Huang Y, Chen G, Feng M, Dai H, Yuan B, Chen X (2019) Effect of heat treatment on hydrophobic silica aerogel. Haranath D, Rao AV, Wagh P (1999) Influence of DCCAs on optical transmittance and porosity properties of TMOS silica aerogels. Gurav JL, Rao AV, Nadargi D, Park H-H (2010b) Ambient pressure dried TEOS-based silica aerogels: good absorbents of organic liquids. Gurav JL, Jung I-K, Park H-H, Kang ES, Nadargi DY (2010a) Silica aerogel: synthesis and applications. įu B, Luo H, Wang F, Churu G, Chu K, Hanan JC, Sotiriou-Leventis C, Leventis N, Lu H (2011) Simulation of the microstructural evolution of a polymer crosslinked templated silica aerogel under high-strain-rate compression. Įhgartner C, Grandl S, Feinle A, Hüsing N (2017) Flexible organofunctional aerogels. ĭurães L, Maia A, Portugal A (2015) Effect of additives on the properties of silica based aerogels synthesized from methyltrimethoxysilane (MTMS). ĭurães L, Ochoa M, Rocha N, Patrício R, Duarte N, Redondo V, Portugal A (2012) Effect of the drying conditions on the microstructure of silica based xerogels and aerogels. ĭorcheh AS, Abbasi M (2008) Silica aerogel synthesis, properties and characterization. Ĭanham LT, Cullis AG, Pickering C, Dosser OD, Cox TI, Lynch TP (1994) Luminescent anodized silicon aerocrystal networks prepared by supercritical drying. The elemental analysis of aerogel confirmed the purity of aerogel while thermogravimetric analysis and differential thermogravimetric analysis revealed its high thermal stability up to 519 ☌.īłaszczyński T, Ślosarczyk A, Morawski M (2013) Synthesis of silica aerogel by supercritical drying method. The aerogel samples were analyzed for their surface hydrophobicity and thermogravimetry analysis. Polyethylene glycol is found to be very effective additive especially for the improvement of the mechanical properties of aerogel, as it has exhibited the breakdown at 21,924.6 N/m 2 with elongation of 0.8 cm. The density of aerogel varied from 0.07 to 0.09 g/cm 3 with increasing amount of additive. This lightweight material has low bulk density, which is found to be affected by the presence of additives. The swelling and de-swelling behavior of aerogel were also analyzed. Polyethylene glycol-based aerogel exhibited high tensile stress-withstanding capacity, at the same time high surface hydrophobicity with contact angle 148°. Methyltrimethoxysilane was used as a precursor in various concentrations to explore the effects on the properties of silica aerogel. Glycerol and polyethylene glycol were used for the synthesis of silica aerogel to improve mechanical and structural properties. Many applications of silica aerogel require desired mechanical and structural properties.
0 Comments
Leave a Reply. |